2014 aluminum alloy
2014 Aluminum alloy chemical Chemical composition
Si: 0.5-1.2% Fe: Max 0.7% Cu:3.9-5.0% Mn:0.4-1.2% Mg:0.2-0.8% Cr:Max 0.1% Zn:Max 0.25% Ti:Max 0.15% Al: remainder
2014 aluminum alloy Mechanical properties
Temper: O
Thickness: 0.5mm-12.5mm Tensile strength :Max 220 Mpa yield strength: Max 110 Mpa elongation: Min 16%
Thickness: 12.5mm-25mm Tensile strength :Max 220 Mpa yield strength: / elongation: /
Temper:T6
Thickness: 0.5mm-1.0mm Tensile strength :Min 450 Mpa yield strength: Min 395 Mpa elongation: Min 6%
Thickness: 1.0mm-6.0mm Tensile strength :Min 455 Mpa yield strength: Min 400 Mpa elongation: Min 7%
Thickness: 6.0mm-12.5mm Tensile strength :Min 460 Mpa yield strength: Min 405 Mpa elongation: Min 7%
Temper:T4
Thickness: 0.5mm-1.0mm Tensile strength :Min 405Mpa yield strength: Min 240 Mpa elongation: Min14%
Thickness: 1.0mm-12.5mm Tensile strength :Min 410 Mpa yield strength: Min 250 Mpa elongation: Min 14%
Temper:T3
Thickness: 0.5mm-1.0mm Tensile strength :Min 405Mpa yield strength: Min 240 Mpa elongation: Min14%
Thickness: 1.0mm-12.5mm Tensile strength :Min 405Mpa yield strength: Min 250 Mpa elongation: Min 14%
Apply to situations requiring high strength and hardness (including high temperature).Aircraft heavy, forgings, thick plates and extruded materials, wheels and structural elements, multi-stage rocket first stage fuel tank and spacecraft parts, truck frame and suspension system parts.